ER55-D2-Ti气体保护焊丝

公司生产的实心气体保护焊丝适合于全位置焊接,能适应较大的焊接电流范围,焊接时电弧稳定、飞溅少 、焊缝成型美观,熔敷效率高,焊缝金属的气孔敏感性低。

Key words:

Product category:

1111

Related products


SLDSJ112


1SLDSJ112 is a fluorine alkali alkaline sintered flux, with gray white circular particles, particle size of 10-60 mesh, and alkalinity of 2.6. It is made from powders such as silicate, carbonate, fluoride, metal oxide, and iron alloy through processes such as balling, low-temperature drying, and high-temperature sintering. The performance of the flux can replace Lincoln's 801 flux in the United States, with beautiful weld formation, smooth surface, no slag inclusion, porosity, and cracks, and good welding process.

SLDSJ601


SLDSJ601 is an alkaline sintered flux for submerged arc welding of stainless steel and heat-resistant steel, with a particle size of 3.0-0.28mm (10-60 mesh). It is used for direct current welding and welding to the positive rod. Stable arc combustion, easy slag removal, beautiful weld formation, and excellent intergranular corrosion resistance of weld metal.

SLDSJ609


SLDSJ609 is a fluorine alkali type high alkalinity low hydrogen sintered flux with an alkalinity of about 2.2. The flux is circular particles with a particle size of 2.0-0.28mm (10-60 mesh). Adopting DC power supply, welding wire connected to positive rod, excellent welding process performance, stable arc, excellent slag removal performance, and beautiful welding formation. The weld seam has excellent crack resistance and high low-temperature impact toughness.

SLDSJ603W


SLDSJ603W is a fluorine-alkali alkaline (B ≈ 2.0) sintered flux, with spherical particles and particle size of 2.0-0.28mm (10-60 mesh). It is used for both AC and DC purposes, with stable arc stability, good high-temperature slag removal performance, and strong resistance to porosity. The flux contains deoxidizers and alloying agents, and the weld seam has excellent low-temperature impact toughness.